STUDIO DI CAMPIONI BI-METALLICI FABBRICATI TRAMITE TECNOLOGIA IBRIDA FUSED DEPOSITION MODELING - FURNACE SINTERING

This thesis aims to analyze and compare bi-metallic samples in 316L-Inconel alloy extruded using FDM fused deposition modeling technology and subsequently heat treated with furnace sintering technology. Specifically, five different deposition strategies will be investigated including co-extrusion through a single nozzle in three different directions and side-by-side co-extrusion of the single filaments through two nozzles, in order to study their behavior at the interface with the related bonding and mechanical and metallurgical properties, compared with those of the single filaments, after the heat treatment of debinding and sintering in the furnace.

La presente tesi si pone come obbiettivo l’analisi e il confronto di campioni bi-metallici in lega 316L-Inconel estrusi mediante tecnologia FDM fused deposition modeling e successivamente trattati termicamente con la tecnologia furnace sintering. Precisamente, verranno indagate cinque diverse strategie di deposizione tra cui co-estrusione tramite un unico ugello in tre differenti direzioni e co-estrusione affiancata dei singoli filamenti tramite due ugelli, al fine di studiarne il comportamento all'interfaccia con il relativo bonding e le proprietà meccaniche e metallurgiche, confrontate con quelle dei singoli filamenti, successivamente al trattamento termico di debinding e sintering in forno.