PEO, or plasma electrolytic oxidation, is a surface conversion process that uses high current density to create a thick layer of protective oxide on the surface of a material. In this study, the effectiveness of various electrolytic baths was evaluated on AlSi10Mg alloy, produced through additive manufacturing, by appropriately modifying an alkaline silicate electrolyte with the addition of additives. The aim was to assess the effect of the incorporation of these additives on the corrosion resistance of the treated samples. The additives considered were: Na2MoO4, (NH4)Mo7O24, CeO2 nanopowder, KMnO4, TiO2, and graphene nanosheets. The results were analyzed using various techniques such as scanning electron microscopy (SEM), X-ray diffraction (XRD), electrochemical impedance spectroscopy (EIS), and potentiodynamic polarization
PEO, plasma electrolytic oxidation, è un processo di conversione superficiale che, attraverso l’applicazione di un’elevata densità di corrente, permette la formazione di uno spesso strato isolante di ossidi superficiali. In questo elaborato, l’efficacia di diversi bagni elettrolitici è stata valutata sulla lega AlSi10Mg, prodotta tramite manifattura additiva, modificando opportunamente un elettrolita silico alcalino mediante l’aggiunta di additivi. L'obiettivo era valutare l'effetto dell'incorporazione degli additivi sulla resistenza alla corrosione dei campioni trattati. Gli additivi considerati sono stati: Na2MoO4, (NH4)Mo7O24, nanopolveri di CeO2, KMnO4, TiO2 e fogli di grafene nanometrici. I risultati ottenuti sono stati valutati utilizzando diverse tecniche di analisi, come osservazioni al microscopio a scansione elettronica (SEM), diffrazione ai raggi X (XRD), spettroscopia di impedenza elettrochimica (EIS) e polarizzazione potentiodinamica.
Studio dell'effetto della funzionalizzazione con inibitori sulla resistenza a corrosione di componenti in lega di alluminio realizzati con tecniche di manifattura additiva e rivestiti mediante processo PEO
VALENTINI, FRANCESCA
2022/2023
Abstract
PEO, or plasma electrolytic oxidation, is a surface conversion process that uses high current density to create a thick layer of protective oxide on the surface of a material. In this study, the effectiveness of various electrolytic baths was evaluated on AlSi10Mg alloy, produced through additive manufacturing, by appropriately modifying an alkaline silicate electrolyte with the addition of additives. The aim was to assess the effect of the incorporation of these additives on the corrosion resistance of the treated samples. The additives considered were: Na2MoO4, (NH4)Mo7O24, CeO2 nanopowder, KMnO4, TiO2, and graphene nanosheets. The results were analyzed using various techniques such as scanning electron microscopy (SEM), X-ray diffraction (XRD), electrochemical impedance spectroscopy (EIS), and potentiodynamic polarizationFile | Dimensione | Formato | |
---|---|---|---|
Studio dell’effetto della funzionalizzazione con inibitori sulla resistenza a corrosione di componenti in lega di alluminio realizzati con tecniche di manifattura additiva e rivestiti mediante processo PEO.pdf
accesso aperto
Dimensione
10.36 MB
Formato
Adobe PDF
|
10.36 MB | Adobe PDF | Visualizza/Apri |
The text of this website © Università degli studi di Padova. Full Text are published under a non-exclusive license. Metadata are under a CC0 License
https://hdl.handle.net/20.500.12608/45931