The thesis work focused on the additive manufacturing of two types of multicomponent silica-based glass, one doped with cerium and the other with lanthanum, in order to respectively increase the photoluminescence and optical properties. Mixtures with different amounts of silica and silica / precursor ratios were prepared and tested by analyzing their rheological properties. The compositions with pseudoplastic behavior were then selected and printed using the technology hybrid uv-direct writing. The samples thus obtained were then heat treated until they were completely sintered. Temperature and holding time have been modified in order to find the suitable treatment to obtain transparent components for both types of multi-component glass. Finally, for silica-lanthanum glass, while the increase in refractive index was analyzed, photoluminescence measurements were carried out for silica-cerium glass.

ll lavoro di tesi si è focalizzato sulla fabbricazione additiva di due tipologie di vetro multicomponente a base silice, uno drogato con cerio e l’altro con lantanio, al fine di aumentarne rispettivamente le proprietà di fotoluminescenza ed ottiche.. Miscele con diverse quantità di silice e rapporti silice/precursore sono state preparate e testate analizzandone le proprietà reologiche. Le composizioni con comportamento pseudoplastico sono state quindi selezionate e stampate utilizzando la tecnologia ibrida estrusione-fotoreticolazione. I campioni così ottenuti sono quindi stati trattati termicamente fino alla completa sinterizzazione. Temperatura e tempo di mantenimento sono stati modificati con lo scopo di trovare il trattamento, adatto per ottenere componenti trasparenti per entrambe le tipologie di vetro multicomponente. Infine, per il vetro silice-lantanio è stato analizzato l’aumento dell’indice di rifrazione mentre per quelli silice-cerio sono state condotte misure di fotoluminescenza.

FABBRICAZIONE ADDITIVA DI VETRO MULTICOMPONENTE TRAMITE UN PROCESSO IBRIDO ESTRUSIONE-FOTORETICOLAZIONE

ZARAMELLA, GIOVANNA
2021/2022

Abstract

The thesis work focused on the additive manufacturing of two types of multicomponent silica-based glass, one doped with cerium and the other with lanthanum, in order to respectively increase the photoluminescence and optical properties. Mixtures with different amounts of silica and silica / precursor ratios were prepared and tested by analyzing their rheological properties. The compositions with pseudoplastic behavior were then selected and printed using the technology hybrid uv-direct writing. The samples thus obtained were then heat treated until they were completely sintered. Temperature and holding time have been modified in order to find the suitable treatment to obtain transparent components for both types of multi-component glass. Finally, for silica-lanthanum glass, while the increase in refractive index was analyzed, photoluminescence measurements were carried out for silica-cerium glass.
2021
HYBRID UV-DIRECT INK WRITING OF MULTICOMPONENT GLASS
ll lavoro di tesi si è focalizzato sulla fabbricazione additiva di due tipologie di vetro multicomponente a base silice, uno drogato con cerio e l’altro con lantanio, al fine di aumentarne rispettivamente le proprietà di fotoluminescenza ed ottiche.. Miscele con diverse quantità di silice e rapporti silice/precursore sono state preparate e testate analizzandone le proprietà reologiche. Le composizioni con comportamento pseudoplastico sono state quindi selezionate e stampate utilizzando la tecnologia ibrida estrusione-fotoreticolazione. I campioni così ottenuti sono quindi stati trattati termicamente fino alla completa sinterizzazione. Temperatura e tempo di mantenimento sono stati modificati con lo scopo di trovare il trattamento, adatto per ottenere componenti trasparenti per entrambe le tipologie di vetro multicomponente. Infine, per il vetro silice-lantanio è stato analizzato l’aumento dell’indice di rifrazione mentre per quelli silice-cerio sono state condotte misure di fotoluminescenza.
Multicomponent glass
ink writing
hybrid uv
File in questo prodotto:
File Dimensione Formato  
Zaramella_Giovanna.pdf

accesso aperto

Dimensione 1.12 MB
Formato Adobe PDF
1.12 MB Adobe PDF Visualizza/Apri

The text of this website © Università degli studi di Padova. Full Text are published under a non-exclusive license. Metadata are under a CC0 License

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12608/36279