Studio dell'austenite residua su perni in 17NiCrMoS6-4

The aim of the thesis is to verify that the pins, characteristic components of an axle, contain residual austenite, quantify it and compare the percentage of residual austenite obtained by quantitative analysis with the X-ray diffractometer with that obtained with an imagej image analysis software. Hardness, surface and 5 mm distance from the surface are also tested on the pins with the universal hardness meter and the effective depth is determined with the microdurometer. In this way it is possible to analyze the hardness values obtained since the law of the decrease in hardness is a function of the carbon gradient, since the pins have been subjected to a carbocementation treatment and a subsequent hardening and tempering treatment.

L’obiettivo della tesi consiste nel verificare che i perni, componenti caratterizzanti di un assale, contengano austenite residua, quantificare tale materiale e confrontare la percentuale di austenite residua ottenuta mediante l’analisi quantitativa con il diffrattometro a raggi X con quella ottenuta con un software di analisi di immagine ImageJ. Le metallografie da utilizzare con il software vengono ottenute tramite un’accurata preparazione del campione e grazie all’utilizzo del microscopio ottico. Vengono inoltre svolte sui perni le prove di durezza, superficiale e a 5 mm di distanza dalla superficie con il durometro universale e viene determinata la profondità efficace con il microdurometro. In questo modo è possibile analizzare i valori di durezza che si ottengono poiché la legge del decremento di durezza è funzione del gradiente di carbonio, essendo i perni stati sottoposti ad un trattamento di carbocementazione e ad un successivo trattamento di tempra e rinvenimento.