In this thesis work, carried out in collaboration with the company Decoral System of Arcole (VR), possible strategies for the valorisation of polyurethane and polyester thermosetting powder paint scraps were investigated. The material under study was the unapplied powder paint, recovered from the plant's spray booths, for which there are currently no outcomes other than start-up to disposal. It has been proposed to use it as a filler for thermosetting matrix composite materials with cold cross-linking. For this purpose, both the powders as they are, directly recovered from the plant, and powders subjected to a preliminary cross-linking and micronization treatment, were mixed in different ratios with epoxy and polyester resin. Samples were obtained by casting in silicone molds, for the execution of the mechanical tests of bending, traction and compression. The thermal behavior of the powders and specimens were also investigated using DSC, the distribution of the filler inside the matrix using SEM and the resistance to the action of light and heat using accelerated aging tests. Powder paint scraps played an effective role as filler in the thermosetting matrix without compromising the properties of the material.

In questo lavoro di tesi, svolto in collaborazione con l’azienda Decoral System di Arcole (VR), sono state indagate possibili strategie di valorizzazione di scarti di vernice in polvere termoindurente di tipo poliuretanica o poliestere. Il materiale oggetto di studio era la vernice in polvere non applicata, recuperata dalle cabine di verniciatura dell’impianto, per cui non esistono attualmente esiti diversi dall'avvio allo smaltimento. E’ stato proposto l’impiego come riempitivo per materiali composti a matrice termoindurente con reticolazione a freddo. A tale scopo, sono state miscelate in rapporti diversi con resina epossidica e poliestere sia le polveri tal quali, direttamente recuperate dall’impianto, sia polveri sottoposte ad un preliminare trattamento di reticolazione e micronizzazione. Sono stati ottenuti dei provini per colata in stampi in silicone, per l’esecuzione dei test meccanici di flessione, trazione e compressione. Sono stati inoltre indagati il comportamento termico delle polveri e dei provini mediante DSC, la distribuzione del riempitivo all’interno della matrice tramite SEM e la resistenza all’azione di luce e calore mediante prove di invecchiamento accelerato. Gli scarti di vernice in polvere hanno svolto un efficace ruolo di riempitivo in matrice termoindurente senza pregiudicare le proprietà di quest’ultimo materiale.

Valorizzazione di scarti di vernice in polvere tramite impiego come riempitivo in matrice termoindurente

DE BIASIO, ARIANNA
2022/2023

Abstract

In this thesis work, carried out in collaboration with the company Decoral System of Arcole (VR), possible strategies for the valorisation of polyurethane and polyester thermosetting powder paint scraps were investigated. The material under study was the unapplied powder paint, recovered from the plant's spray booths, for which there are currently no outcomes other than start-up to disposal. It has been proposed to use it as a filler for thermosetting matrix composite materials with cold cross-linking. For this purpose, both the powders as they are, directly recovered from the plant, and powders subjected to a preliminary cross-linking and micronization treatment, were mixed in different ratios with epoxy and polyester resin. Samples were obtained by casting in silicone molds, for the execution of the mechanical tests of bending, traction and compression. The thermal behavior of the powders and specimens were also investigated using DSC, the distribution of the filler inside the matrix using SEM and the resistance to the action of light and heat using accelerated aging tests. Powder paint scraps played an effective role as filler in the thermosetting matrix without compromising the properties of the material.
2022
Upgrade of powder coating waste as filler for thermoset matrices
In questo lavoro di tesi, svolto in collaborazione con l’azienda Decoral System di Arcole (VR), sono state indagate possibili strategie di valorizzazione di scarti di vernice in polvere termoindurente di tipo poliuretanica o poliestere. Il materiale oggetto di studio era la vernice in polvere non applicata, recuperata dalle cabine di verniciatura dell’impianto, per cui non esistono attualmente esiti diversi dall'avvio allo smaltimento. E’ stato proposto l’impiego come riempitivo per materiali composti a matrice termoindurente con reticolazione a freddo. A tale scopo, sono state miscelate in rapporti diversi con resina epossidica e poliestere sia le polveri tal quali, direttamente recuperate dall’impianto, sia polveri sottoposte ad un preliminare trattamento di reticolazione e micronizzazione. Sono stati ottenuti dei provini per colata in stampi in silicone, per l’esecuzione dei test meccanici di flessione, trazione e compressione. Sono stati inoltre indagati il comportamento termico delle polveri e dei provini mediante DSC, la distribuzione del riempitivo all’interno della matrice tramite SEM e la resistenza all’azione di luce e calore mediante prove di invecchiamento accelerato. Gli scarti di vernice in polvere hanno svolto un efficace ruolo di riempitivo in matrice termoindurente senza pregiudicare le proprietà di quest’ultimo materiale.
prove meccaniche
powder coating
DSC
termoindurenti
riempitivo
File in questo prodotto:
File Dimensione Formato  
De Biasio_Arianna.pdf

accesso aperto

Dimensione 5.99 MB
Formato Adobe PDF
5.99 MB Adobe PDF Visualizza/Apri

The text of this website © Università degli studi di Padova. Full Text are published under a non-exclusive license. Metadata are under a CC0 License

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/20.500.12608/51858