Analysis of microstructure and thermal properties of coated and uncoated Al-Si alloys

Nowadays there is a growing demand for aluminum materials that can be used in several applications for its suitable properties. In particular, together with Silicon, it is applied as a good performer in the foundry work. The aim of this project deals with the study of the microstructure and thermal properties of the aluminium alloys with 9% of silicon. The analysed properties are thermal conductivity, thermal diffusivity and specific heat in terms of output power and measuring time. They are studied with the Hot Disk machine and the TPS method. These analysis highlight that the best combinations between the two physical parameters are calculated with the Slab Method and the thermal conductivity and the thermal diffusivity are independent of the power.

Al giorno d'oggi c'è una crescente domanda di materiali a base di alluminio che possono essere utilizzati in diverse applicazioni grazie alle loro proprietà come nell’ambito della fonderia, insieme al silicio. L'obiettivo di questo progetto di tesi è lo studio della microstruttura e delle proprietà termiche delle leghe di alluminio con il 9% di silicio. Le proprietà analizzate sono la conducibilità termica, la diffusività termica e il calore specifico in termini di potenza e tempo di misurazione. Sono state studiate con la macchina Hot Disk e il metodo TPS. Queste analisi evidenziano che le migliori combinazioni tra i due parametri fisici sono calcolate con il metodo Slab e che la conduttività termica e la diffusività termica sono indipendenti dalla potenza applicata.