Progettazione di prove sperimentali per lo studio dell'effetto Bauschinger su acciai strutturali

In this work an experimental test procedure was defined for the study of the Bauschinger effect on structural steels. The Bauschinger effect is described as a decrease in the resistance of the material following a plastic deformation of the opposite sign. To study the Bauschinger effect, tests were performed on samples of C40 steel with the MTS-322 testing machine at the mechanical engineering laboratory. The samples were subjected to a tensile phase, up to a certain total deformation value, different for each sample, followed by a compression phase and finally an unloading phase. To quantify the Bauschinger effect presented by the samples, indicators measurable from the experimental stress-strain curves obtained from the tests were used.

In questo lavoro è stata definita una procedura di prova sperimentale per lo studio dell'effetto Bauschinger su acciai strutturali. L'effetto Bauschinger viene descritto come una diminuzione della resistenza del materiale in seguito ad una deformazione plastica di segno opposto. Per lo studio dell'effetto Bauschinger sono stati eseguiti dei test su campioni di acciaio C40 con la macchina di prova MTS-322 presso il laboratorio di ingegneria meccanica. I campioni sono stati sottoposti ad una fase di trazione, fino ad un certo valore di deformazione totale, diverso per ciascun campione, seguita da una fase di compressione ed infine da una fase di scarico. Per quantificare l'effetto Bauschinger presentato dai campioni, sono stati utilizzati degli indicatori misurabili dalle curve sperimentali sforzo-deformazione ottenute dalle prove.