The aim of the thesis is the observation of the emissions produced by a regenerative melting furnace in the glass production process. The feeding conditions were varied, in particular the excess of air respect to the stoichiometric combustion ratio, then observing the trends in the concentrations of carbon monoxide (CO), nitrogen oxides (NOx) and sulfur dioxide (SO2). Carbon monoxide derives from the use of methane as a fuel, nitrogen oxides from the use of atmospheric air as a comburent and finally sulfur dioxide because sodium sulphate (Na2SO4) is used for the refining phase. Finally, the SFC (Sonic Flow Control) system was put into operation by observing how it acts inside the furnace, with the effect of a global reduction in the emissions generated, making combustion more efficient and optimised.

Lo scopo dell'elaborato è l'osservazione delle emissioni prodotte da un forno fusorio di tipo rigenerativo nel processo di produzione del vetro. Sono state variate le condizioni di alimentazione, in particolare l'eccesso d'aria rispetto al rapporto stechiometrico di combustione, andando poi ad osservare gli andamenti delle concentrazioni di monossido di carbonio(CO), ossidi di azoto(NOx) e anidride solforosa(SO2). Il monossido di carbonio deriva dall'utilizzo del metano come combustibile, gli ossidi di azoto dall'utilizzo di aria atmosferica come comburente e infine l'anidride solforosa perché viene utilizzato solfato di sodio(Na2SO4) per la fase di affinaggio. Infine è stato messo in funzione l'impianto SFC(Sonic Flow Control) andando ad osservare come esso agisce all'interno del forno, con l'effetto di una riduzione globale delle emissioni generate, rendendo la combustione più efficiente ed ottimizzata.