Studio dei trattamenti termici per nitinol martensitico prodotto con Additive Manufacturing

In this study it has been analysed the change on properties of a martensitic nitinol cylinder (Ni 50.1%, Ti 49.9%) obtained with LPBF by varying the heat treatments executed on it. The considered properties are: transformation temperatures, hardness and elastic module. The samples were annealed for 4 or 1 hour at 1050 °C and then cooled in water or oven; the sample annealed for 1 hour was then aged for 3 hours at 600 °C, 450 °C and 300 °C, and then air cooled. For the analysis of the properties, a DSC was used for the transformation temperatures and a nanoindenter for hardness and the elastic module. Microstructure was then analysed using a microscope.

In questo studio è stato analizzato il cambiamento delle proprietà di un cilindro di nitinol martensitico (Ni 50.1%, Ti 49.9%) ottenuto tramite LPBF al variare dei trattamenti termici eseguiti su di esso. Le proprietà considerate sono: temperature di trasformazione, durezza e modulo elastico. I campioni hanno subito una solubilizzazione per 4 o 1 ora a 1050 °C con raffreddamento in acqua o in forno; il campione solubilizzato per 1 ora è stato poi invecchiato per 3 ore a 600 °C, 450 °C e 300 °C e raffreddato poi in aria. Per l’analisi delle proprietà, è stata usata una DSC per le temperature di trasformazione e un nanoindentatore per durezza e modulo elastico. La microstruttura è stata poi analizzata attraverso un microscopio.