Sintesi di poliacrilati biodegradabili tramite co-polimerizzazione radicalica

Among the most popular commodity plastics diffuse nowadays, acrylic polymers include a wide range of materials used as coatings, paints, adhesives, biomedical materials and textiles. Despite their interesting properties, these polymers are problematic from the environmental point of view because the main polymer chain consists entirely of carbon atoms, which makes them highly resistant to degradation and therefore difficult to recycle. In this Thesis project a monomer, Oxoditiepan-2-one (OTP), was synthesized. This monomer can be incorporated by radical polymerization within acrylic matrices. This allows the introduction of a labile group such as the ester group in the main polymer chain, which can be easily hydrolyzed, making the copolymer (bio)degradable.

Tra le materie plastiche più diffuse al giorno d’oggi, i polimeri acrilici comprendono un'ampia gamma di materiali impiegati come rivestimenti, vernici, adesivi, materiali biomedici e tessili. Nonostante le interessanti proprietà, questi polimeri risultano problematici dal punto di vista ambientale in quanto la catena polimerica principale è costituita interamente di atomi di carbonio, che li rende altamente resistenti alla degradazione e quindi difficili da riciclare. In questo progetto di Tesi è stato sintetizzato un monomero, l’Ossoditiepan-2-one (OTP), il quale può essere incorporato mediante copolimerizzazione radicalica all’interno di matrici acriliche. Questo permette di introdurre all’interno della catena polimerica principale un gruppo labile come il gruppo estereo, facilmente idrolizzabile, rendendo il copolimero (bio)degradabile.